铜表面导电薄膜的制备及其腐蚀性能研究_金属材料工程.rar

资料分类:工业大学 上传会员:艾薇儿 更新时间:2013-07-10
需要金币1000 个金币 资料包括:完整论文 下载论文
转换比率:金额 X 10=金币数量, 例100元=1000金币 论文字数:17468
折扣与优惠:团购最低可5折优惠 - 了解详情 论文格式:Word格式(*.doc)

摘要:本论文研究了导电聚合物涂层作为交换膜燃料电池(PEMFC)铜双极板的表面抗腐蚀涂层的抗腐蚀性能,对比研究了以对甲苯磺酸(ToSH)为掺杂剂的吡咯溶液以及没有掺杂剂的吡咯溶液中,采用循环伏安法在铜电极表面聚合得到聚吡咯(Ppy)涂层。讨论了掺杂剂的用量,结果表明在掺杂0.1MToSH的0.2MPpy+0.2MH2C2O4电沉积溶液中效果最佳。采用红外光谱(IR)、扫描电子显微镜(SEM)等表面分析方法对导电聚合物涂层特征进行表征,表明掺杂Ppy涂层由小颗粒紧密排列而成,外观光亮、平整。未掺杂Ppy涂层局部致密但不平整,出现少量空隙与裂缝。采用动电位极化、开路电位-时间曲线以及电化学阻抗谱(EIS)等电化学测量技术评价所制涂层的耐蚀性能,表明两种方法制备的Ppy涂层对铜基体都有很好的防护性能,其中未掺杂Ppy涂层使得铜基体自腐蚀电位正移了61mV,腐蚀电流密度从10-4A/cm2下降到10-5A/cm2;而掺杂Ppy膜使得基体自腐蚀电位正移了76mV,腐蚀电流密度从10-4A/cm2下降到10-5A/cm2。这是由于未掺杂涂层存在微缺陷,而掺杂涂层相对致密,涂层对基体的保护时间更长,耐蚀性能更好。

关键词: 聚吡咯,对甲苯磺酸,掺杂,腐蚀

 

Abstract:In this research, corrosion resistance of the conductive polymer coating as the surface anti-corrosion coating of the copper bipolar plate of the exchange membrane fuel cell (PEMFC) was studied, comparing the pyrrole solution  with  p-toluenesulfonic acid (ToSH) pyrrole as the dopant with the pyrrole solution  without  p-toluenesulfonic acid (ToSH) pyrrole. The poly pyrrole coating of the surface of the copper electrode was got by using the cyclic voltammetry polymerization . The amount of dopant was discussed. It was resulted that 0.2Mpy +0.2 MH2C2O4 power deposition solution with 0.1MtoSH was the best . the conductive polymer coating characteristics were characterized by Infrared spectroscopy (IR), scanning electron microscopy (SEM) and other surface analysis methods . It showed that the coating doping PPy was consisted of closely arranged small particles in bright and smooth appearance. The coating undoping PPy was dense locally but not flat. A little of gaps and cracks were appeared . By using the electrochemical measurements techniques , such as potentiodynamic polarization, open circuit potential - time curves and electrochemical impedance spectroscopy (EIS) , the corrosion resistance of the coating was evaluated.  It showed that Ppy coating ,Prepared by two methods has a good protective performance to the copper substrate. The corrosion potential of the copper substrate with Undoped Ppy coating shifted 61mV positively, and the corrosion current density decreased from 10-4A/cm2 to 10-5A/cm2. The corrosion potential of the substrate with the Ppy membrane, synthesized by cyclic voltammetry, shifted 76mV positively, the corrosion current density decreased from 10-4A/cm2 to 10-5A/cm2. This is due to that the undoped coating has the micro-defects , while the doped coating is relatively dense, the protection time of coating on the substrate is longer, and corrosion resistance is better.

Key words : Ppy, ToSH, Doping, Corrosion

 

相关论文资料:
最新评论
上传会员 艾薇儿 对本文的描述:研究了导电聚合物涂层作为交换膜燃料电池(PEMFC)铜双极板的表面抗腐蚀涂层的抗腐蚀性能,对比研究了以对甲苯磺酸(ToSH)为掺杂剂的吡咯溶液以及没有掺杂剂的吡咯溶液中,采用循环伏......
发表评论 (我们特别支持正能量传递,您的参与就是我们最好的动力)
注册会员后发表精彩评论奖励积分,积分可以换金币,用于下载需要金币的原创资料。
您的昵称: 验证码: